DUTC - Disc ultra-translucent colored

Zirconium milling blanks with a diameter of 98 mm in a variety of thicknesses between 10 and 25 mm in a variety of colors

Translucency (%)                             42

Flexural strength (Mpa)              1200

Material classification                 3 mol%

                                                          Zirconium oxide, yittrium oxide stabilized

chem. composition                      ZrO2+HfO2+Y203 ≥99% 

                                                          Y203<6%

Classification according to

ISO 6872                                        Type II, Class 6

Indications                                     Fully anatomical crown,

                                                          Bridge

                                                          (max. 16 unit bridge, the absence of neighboring teeth may be 3 units

                                                          in the anterior and 2 units in the posterior region),

                                                          Inlay,

                                                          Venner,

                                                          partially or completely veneered ceramic crown and bridge,

                                                          telescopic crown and custom abutment

Flexural strength / crack

toughness MPa*m1/2               >6

thermal expansion

coefficient 10-6 K-1g                10,5   

Modulus of elasticity (GPa)      >200

Density in sintered

Condition (g/cm3)                      >6

Available in different colors in the following sizes: 10, 12, 14, 16, 18, 20, 22 and 25 mm thickness

Disc DUTC ø 98 mm 10 mm

Disc DUTC ø 98 mm 12 mm

Disc DUTC ø 98 mm 14 mm

Disc DUTC ø 98 mm 16 mm

Disc DUTC ø 98 mm 18 mm

Disc DUTC ø 98 mm 20 mm

Disc DUTC ø 98 mm 22 mm

Disc DUTC ø 98 mm 25 mm