TT - translucent high strength with color gradient

Zirconium milling blanks with a diameter of 98 mm in a variety of thicknesses between 10 and 25 mm in a variety of colors

Translucency (%)                            42-49

Flexural strength (Mpa)              1100-700

Material classification                5 mol%

                                                          tetragonal zirconium oxide, yittrium oxide stabilized

Material-Klassifikation               5 mol%

                                                          cubic / tetragonales Zirkonoxid, Yittriumoxid-teilstabilisiert

chem. composition                      ZrO2+HfO2+Y203 ≥99% 

                                                          Y203<6%

Classification according to

ISO 6872                                        Type II, Class 5

Indications                                     Fully anatomical crown,

                                                          Bridge (max. three-part),     

                                                          Inlay,

                                                          Venner,

                                                          telescopic crown

Flexural strength / crack

toughness MPa*m1/2               >4

thermal expansion

coefficient 10-6 K-1g                10

Modulus of elasticity (GPa)      >200

Density in sintered

Condition (g/cm3)                      >6

Available in different colors in the following sizes: 10, 12, 14, 16, 18, 20, 22 and 25 mm thickness